PROPIEDADES DE LA MADERA BALSA PARA EL DISEO DE PUENTES
FUENTE 1
compresion Traccin
g/cm3 kg/cm2 kg/cm2
menor a 0.08 47 77 4670 (+-)720 12970 (+-)4580
entre 0.08 y 0.014 123 202
mas de 0.14 198 327
http://www.amaglider.com/?p=view&a=balsa-wood-properties
FUENTE 2
compresion Traccin
g/cm3 kg/cm2 kg/cm2
baja 0.075 48 78 4690 (+-)720 13000 (+-)4590
media 0.15 123 202
alta 0.225 199 328
FUENTE 3 Ensayos en la Universidad de Texas
Tabla 3. RESISTENCIA A LA COMPRESIN
Densidadr (g/cm2) sAL (Kg/cm2) sAP (Kg/cm2)
0.1 65 49
0.14 125 97
0.21 215 154
0.25 287 196
0.32 401 253
http://www.sciencedirect.com/science/article/pii/S0020768307002727
Donde:sAL
sAP
Esfuerzo Lmite
Esfuerzo de strees
MODULO DE ELASTICIDADEZFUERZOS PRINCIPALES
EZFUERZOS PRINCIPALES MODULO DE ELASTICIDAD
LIMITES
DENSIDAD
kg/cm2 kg/cm2
DENSIDAD
kg/cm2 kg/cm2
compresion Traccin
compresion Traccin
65
125
215
287
401
49 97
154 196
253
0
100
200
300
400
500
0.1 0.14 0.21 0.25 0.32
Res
iste
nci
a a
la C
om
pre
sio
n (
kg/c
m2)
Densidad de la Madera (g/cm3)
Resistencia a la Compresion
sAL sAP
-
ENSAYOS
Ensayos con contenido de humedad 9 a 12%
Probetas rectangulares de 1pulgX1pulgX3pulg (ALTA DENSIDAD)
Probetas rectangulares de 1.5pulgX1.5pulgX3pulg (BAJA DENSIDAD)Se considera una densidad de referencia rs=1.5g/cm3
Densidad Relativa (r/rss)
MODULO DE ELASTICIDAD para diferentes densidades de mader balsa
r/rs E A ksi (GPa) r/rs
E R ksi
(MPa) r/rs
E T ksi
(MPa) r/rs
T AR ksi
(MPa) r/rs
T AT ksi
(MPa)
0.043 88 (0.61) 0.049 5.02 (34.6) 0.047 2.74 (18.9) 0.043 5.72 (39.5) 0.049 6.37 (43.9)
0.079 289 (1.99) 0.085 12.77 (88.1) 0.076 3.50 (24.1) 0.086 15.87 (109.4) 0.092 13.00 (89.6)
0.097 441 (3.04) 0.125 35.76 (246.6) 0.111 7.96 (54.9) 0.121 29.10 (200.6) 0.14 19.39 (133.7)
0.128 815 (5.62) 0.145 50.07 (345.2) 0.13 11.44 (78.9) 0.141 38.99 (268.8) 0.203 21.67 (149.4)
0.158 960 (6.62) 0.156 62.12 (428.3) 0.15 14.25 (98.3) 0.207 51.61 (355.9) 0.242 35.36 (243.8)
EZFUERZO A COMPRESION para diferentes densidades de mader balsa
r/rs
sAL ksi
(MPa)
sAP ksi
(MPa) r/rs
syR psi
(MPa) r/rs
syT psi
(MPa) r/rs Tpsi (MPa) r/rs
T ATF psi
(MPa)
0.065 0.92 (6.4) 0.70 (4.8) 0.044 63 (0.43) 0.047 48 (0.33) 0.044 132 (0.91) 0.05 96 (0.66)
0.096 1.78 (12.3) 1.37 (9.45) 0.086 103 (0.710) 0.077 81 (0.56) 0.1 298 (2.05) 0.1 212 (1.46)
0.137 3.06 (21.1) 2.19 (15.1) 0.118 171 (1.18) 0.111 109 (0.752) 0.141 449 (3.10) 0.14 312 (2.15)
0.165 4.07 (28.1) 2.79 (19.2) 0.135 198 (1.37) 0.15 124 (0.855) 0.163 526 (3.63) 0.188 421 (2.90)
0.215 5.70 (39.3) 3.59 (24.8) 0.16 236 (1.63) 0.169 180 (1.24) 0.207 736 (5.07) 0.242 541 (3.73)
COMPRESIN CORTE
COMPRESIN CORTE (CIZALLAMIENTO)
AXIAL RADIAL TANGENCIAL Axial radial Axial Tangencial
Grafico: Modulo de Elasticidad Axial en funcion de la
Densidad Relativa
RADIAL TANGENCIAL Axial radial Axial TangencialAXIAL
-
COMPRESION AXIAL
Grafico: Esfuerzos a compresin axial principales (sAL,sAP) en
funcion de la Deformacin
ENSAYOS
-
Grafico: A densidades mas bajas la diferencia entre el stress y la
Tensin Lmite de Meseta es Relativamente Pequeo pero esta
diferencia aumenta con la densidad. (61 experimentos)
Grafico: Esfuerzo a compresin axial en funcion de la Densidad
Relativa (61 experimentos)
-
CIZALLADURA
Maquina para el ensayo a cizalladura
Comparacin de respuestas de Cizallaje radial y
Tangencial (29 ensayos)
Comparacin de respuestas de Cizallaje radial y
Tangencial (29 ensayos) a diferentes densidades.